SAF-T-EZE®
GP Aircraft Grade Anti-Seize is compounded from graphite and
petroletum to satisfy the requirements of MIL-T-5544 for use on threaded
joints.
|
|
SAF-T-EZE® ZP Aircraft
Grade Anti-Seize is
compounded from zinc and petroletum to meet MIL-T-22361 requirements for
use on threaded steel parts assembled in aluminum or zinc castings. SAF-T-EZE
Aircraft grades Anti-Seize are also used in other than aircraft
precision applications. They do not contain lead, copper or molybdenum
disulfide. Certificates of conformance are available for each batch. |
|
| |
|
|
|
|
GRAPHITE/PETROLETUM
ANTI-SEIZE
Exceeds
MIL-T-5544 |
| Characteristic |
Product |
Packaging |
BASIC
COMPOSITION: GRAPHITE/PETROLETUM
COLOR: BLACK
TEMPERATURE: 6500°F.
NLGI GRADE: 1
SPECIFIC GRAVITY: 1.2
WEIGHT PER GALLON: 9.16 LBS
FLASH POINT: C.O.C. >250°F.
PENETRATION: 260-300
PARTICLE SIZE: 1 MIL
|
GP-16
|
16
OZ CAN
|
| Application |
Can
be used as a lubricant, a sealer, a break in lubricant,
a tapping compound on plastics as well as metals.
Surface need not be cleaned before application unless
grit or low quality oil/grease is present and ultimate
performance is required. The reduction in assembly
friction increases torque tension by about 20%. Use on
threaded parts, bushings, gears, valve stems, chain
sprockets, levers, hinges, pivots, rollers, heat
exchanger or manifold bolts, or as a gasket release
agent, etc.
NOTE: This product is not recommended for
pure oxygen systems. |
|
|
|
|
|
|
|
|
ZINC/PETROLETUM
ANTI-SEIZE
Meets
MIL-T-22361 |
| Characteristic |
Product
Name |
Packaging |
BASIC
COMPOSITION: ZINC/PETROLETUM
COLOR: SILVER GRAY
TEMPERATURE: -65
TO 750°F.
NLGI GRADE: 1
SPECIFIC GRAVITY: 1.2
WEIGHT PER GALLON: 9.16 LBS
FLASH POINT: C.O.C. 360°F.
PENETRATION: 175-200
PARTICLE SIZE: 1 MIL. MAXIMUM
|
ZPBT-8
ZPBT-16
|
8
OZ BRUSH TOP
16 OZ BRUSH TOP
|
| Application |
Can
be used as a lubricant, a sealer, a break in lubricant, a
tapping compound on plastics as well as metals. Surface
need not be cleaned before application unless grit or low
quality oil/grease is present and ultimate performance is
required. The reduction in assembly friction increases
torque tension by about 20%. Use on threaded parts,
bushings, gears, valve stems, chain sprockets, levers,
hinges, pivots, rollers, heat exchanger or manifold bolts,
or as a gasket release agent, etc.
NOTE: This product is not recommended for pure
oxygen systems. |
|
|
|
|